Ti dyamèt 225mm founo grafit elektwòd itilize pou pwodiksyon Carborundum rafine founo elektrik
Paramèt teknik
Tablo 1: Paramèt teknik pou ti Dyamèt Graphite Electrode
| Dyamèt | Pati | Rezistans | Fòs flexural | Modil jèn | Dansite | CTE | Ash | |
| Pous | mm | μΩ·m | MPa | GPa | g/cm3 | ×10-6/℃ | % | |
| 3 | 75 | Elektwòd | 7.5-8.5 | ≥9.0 | ≤9.3 | 1.55-1.64 | ≤2.4 | ≤0.3 |
| Pwent tete | 5.8-6.5 | ≥16.0 | ≤13.0 | ≥1.74 | ≤2.0 | ≤0.3 | ||
| 4 | 100 | Elektwòd | 7.5-8.5 | ≥9.0 | ≤9.3 | 1.55-1.64 | ≤2.4 | ≤0.3 |
| Pwent tete | 5.8-6.5 | ≥16.0 | ≤13.0 | ≥1.74 | ≤2.0 | ≤0.3 | ||
| 6 | 150 | Elektwòd | 7.5-8.5 | ≥8.5 | ≤9.3 | 1.55-1.63 | ≤2.4 | ≤0.3 |
| Pwent tete | 5.8-6.5 | ≥16.0 | ≤13.0 | ≥1.74 | ≤2.0 | ≤0.3 | ||
| 8 | 200 | Elektwòd | 7.5-8.5 | ≥8.5 | ≤9.3 | 1.55-1.63 | ≤2.4 | ≤0.3 |
| Pwent tete | 5.8-6.5 | ≥16.0 | ≤13.0 | ≥1.74 | ≤2.0 | ≤0.3 | ||
| 9 | 225 | Elektwòd | 7.5-8.5 | ≥8.5 | ≤9.3 | 1.55-1.63 | ≤2.4 | ≤0.3 |
| Pwent tete | 5.8-6.5 | ≥16.0 | ≤13.0 | ≥1.74 | ≤2.0 | ≤0.3 | ||
| 10 | 250 | Elektwòd | 7.5-8.5 | ≥8.5 | ≤9.3 | 1.55-1.63 | ≤2.4 | ≤0.3 |
| Pwent tete | 5.8-6.5 | ≥16.0 | ≤13.0 | ≥1.74 | ≤2.0 | ≤0.3 | ||
Tablo 2: Kapasite aktyèl pou pote ti Dyamèt Graphite Electrode
| Dyamèt | Chaj aktyèl | Dansite aktyèl la | Dyamèt | Chaj aktyèl | Dansite aktyèl la | ||
| Pous | mm | A | A/m2 | Pous | mm | A | A/m2 |
| 3 | 75 | 1000-1400 | 22-31 | 6 | 150 | 3000-4500 | 16-25 |
| 4 | 100 | 1500-2400 | 19-30 | 8 | 200 | 5000-6900 | 15-21 |
| 5 | 130 | 2200-3400 | 17-26 | 10 | 250 | 7000-10000 | 14-20 |
Tablo 3: Graphite Electrode Size & Tolerans Pou Ti Dyamèt Graphite Electrode
| Dyamèt nominal | Dyamèt aktyèl (mm) | Longè nominal | Tolerans | |||
| Pous | mm | Max. | Min. | mm | Pous | mm |
| 3 | 75 | 77 | 74 | 1000 | 40 | -75 ~ + 50 |
| 4 | 100 | 102 | 99 | 1200 | 48 | -75 ~ + 50 |
| 6 | 150 | 154 | 151 | 1600 | 60 | ± 100 |
| 8 | 200 | 204 | 201 | 1600 | 60 | ± 100 |
| 9 | 225 | 230 | 226 | 1600/1800 | 60/72 | ± 100 |
| 10 | 250 | 256 | 252 | 1600/1800 | 60/72 | ± 100 |
Ti Dyamèt Graphite Electrodes Karakteristik
1.compact gwosè
2.Superior Rezistans Chalè
3.Excellent konduktivite
4.Short Prechofaj Tan
Aplikasyon prensipal la
- carbure kalsyòm fusion
- Pwodiksyon Carborundum
- Corundum raffinage
- Metal ra fusion
- Ferrosilicon plant refractory
Avantaj Gufan
Ti dyamèt elektwòd grafit nou yo ap revolusyone endistri fusion.Gwosè kontra enfòmèl ant yo, rezistans chalè siperyè, konduktivite ekselan, ak adaptabilite fè yo trè apwopriye pou operasyon fusion presizyon.Avèk rezistans yo, inifòmite, tan prechofaj rapid, ak efikasite enèji, elektwòd nou yo asire pwosesis SMELTING efikas ak efikas, ki pèmèt ou reyalize rezilta optimal nan operasyon ou yo.Chwazi ti elektwòd grafit dyamèt nou yo epi fè eksperyans diferans nan operasyon fondri ou yo.