Ti Dyamèt Graphite Electrodes Rod pou founo elektrik Arc nan asye ak endistri fondri
Paramèt teknik
Tablo 1: Paramèt teknik pou ti Dyamèt Graphite Electrode
| Dyamèt | Pati | Rezistans | Fòs flexural | Modil jèn | Dansite | CTE | Ash | |
| Pous | mm | μΩ·m | MPa | GPa | g/cm3 | ×10-6/℃ | % | |
| 3 | 75 | Elektwòd | 7.5-8.5 | ≥9.0 | ≤9.3 | 1.55-1.64 | ≤2.4 | ≤0.3 |
| Pwent tete | 5.8-6.5 | ≥16.0 | ≤13.0 | ≥1.74 | ≤2.0 | ≤0.3 | ||
| 4 | 100 | Elektwòd | 7.5-8.5 | ≥9.0 | ≤9.3 | 1.55-1.64 | ≤2.4 | ≤0.3 |
| Pwent tete | 5.8-6.5 | ≥16.0 | ≤13.0 | ≥1.74 | ≤2.0 | ≤0.3 | ||
| 6 | 150 | Elektwòd | 7.5-8.5 | ≥8.5 | ≤9.3 | 1.55-1.63 | ≤2.4 | ≤0.3 |
| Pwent tete | 5.8-6.5 | ≥16.0 | ≤13.0 | ≥1.74 | ≤2.0 | ≤0.3 | ||
| 8 | 200 | Elektwòd | 7.5-8.5 | ≥8.5 | ≤9.3 | 1.55-1.63 | ≤2.4 | ≤0.3 |
| Pwent tete | 5.8-6.5 | ≥16.0 | ≤13.0 | ≥1.74 | ≤2.0 | ≤0.3 | ||
| 9 | 225 | Elektwòd | 7.5-8.5 | ≥8.5 | ≤9.3 | 1.55-1.63 | ≤2.4 | ≤0.3 |
| Pwent tete | 5.8-6.5 | ≥16.0 | ≤13.0 | ≥1.74 | ≤2.0 | ≤0.3 | ||
| 10 | 250 | Elektwòd | 7.5-8.5 | ≥8.5 | ≤9.3 | 1.55-1.63 | ≤2.4 | ≤0.3 |
| Pwent tete | 5.8-6.5 | ≥16.0 | ≤13.0 | ≥1.74 | ≤2.0 | ≤0.3 | ||
Tablo 2: Kapasite aktyèl pou pote ti Dyamèt Graphite Electrode
| Dyamèt | Chaj aktyèl | Dansite aktyèl la | Dyamèt | Chaj aktyèl | Dansite aktyèl la | ||
| Pous | mm | A | A/m2 | Pous | mm | A | A/m2 |
| 3 | 75 | 1000-1400 | 22-31 | 6 | 150 | 3000-4500 | 16-25 |
| 4 | 100 | 1500-2400 | 19-30 | 8 | 200 | 5000-6900 | 15-21 |
| 5 | 130 | 2200-3400 | 17-26 | 10 | 250 | 7000-10000 | 14-20 |
Avantaj
1.Tretman anti-oksidasyon pou lonjevite.
2.High-pite, segondè-dansite, estabilite chimik fò.
3.High D presizyon, bon sifas fini.
4.High fòs mekanik, ba rezistans elektrik.
5.Resistant nan fann & eklatman.
6.High rezistans nan oksidasyon ak chòk tèmik.
Aplikasyon prensipal la
- carbure kalsyòm fusion
- Pwodiksyon Carborundum
- Corundum raffinage
- Metal ra fusion
- Ferrosilicon plant refractory
RP Graphite Electrode Pwosesis Pwodiksyon
Règ kalite sifas
1.Defo yo oswa twou yo pa ta dwe plis pase de pati sou sifas elektwòd grafit la, ak domaj yo oswa gwosè twou yo pa dwe pèmèt depase done ki nan tablo ki anba a mansyone.
2.Pa gen okenn krak transverse sou sifas elektwòd la.Pou krak longitudinal, longè li yo ta dwe pa plis pase 5% nan sikonferans elektwòd grafit la, lajè li yo ta dwe nan 0.3-1.0mm ranje.Done krak lonjitidinal anba a 0.3mm done yo ta dwe dwe neglijab
3.Lajè zòn ki graj tach (nwa) sou sifas elektwòd grafit la ta dwe pa mwens pase 1/10 nan sikonferans elektwòd grafit la, ak longè zòn ki graj (nwa) plis pase 1/3 nan longè elektwòd grafit. pa gen dwa.